HRC58 Hardness Boltless Ball Mill Liners For Grinding Fine CaCO3 Powder manufacturer from China Wuxi Orient Anti-wear Engineering Co.,Ltd

HRC58 Hardness Boltless Ball Mill Liners For Grinding Fine CaCO3 Powder

Place of Origin:

Jiangsu, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Place of Origin: Jiangsu, China (Mainland)
Brand Name: Chen's Liner
Model Number: DF034
Application: grinding fine CaCO3 powder

Detailed Product Description

HRC58 Hardness Boltless Ball Mill Liners For Grinding Fine CaCO3 Powder

Quick Details

1.Hardness: more than HRC58
2.Capacity increase
3.Size check: by steel templates
4.Internal quality check: by UT tester

Boltless Mill Liners for Grinding Fine CaCO3 Powder Description:

In 1994, we designed the first super fine powder pulverizing ball mill production line and the boltless ball mill liners applicable to the super fine pulverizing field in China, which can achieve ideal output on the fineness of finished products with 2μm∼90μm.

In Φ2.2 x 6m ball mill, the capacity is 3.2mt per hour on 2μm∼10μm, which has achieved leading level at home and abroad.

In 2000, we designed the first set of the boltless liners applied in a super fine powder vibrating mill in China.

In 2003, we designed and manufactured ball mill liners used in the largest super fine powder ball mills for Anhui Guofeng Nonmetal Hi-tech Material Co.(Jiuhua Calcium Co.) in China.

Ball mill super fine powder pulverizing process mainly relies on liners.

In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.

Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

Chemical Composition & Mechanical Property of Wear-resistant Castings

Item	Cr-Mo Alloy Steel I	Cr-Mo Alloy Steel II	Cr-Mo Alloy Steel III	High Cr white iron	High Cr Alloy Steel	High Manganese Steel	Ni-Hard cast iron
C	0.30~0.50	0.65~0.90	0.40~0.90	2.40~3.20	1.1~2.2	0.90~1.30	2.40~3.60
Si	0.50~1.20	≤0.75	0.70~1.20	0.60~1.20	0.60~1.20	≤0.08	≤0.80
Mn	0.40~1.20	0.50~1.20	0.60~1.00	0.50~1.00	0.50~1.00	11.00~18.00	≤2.0
Cr	1.70~2.50	1.50~2.50	4.00~7.00	12.00~30.00	11.00~30.00	1.50~2.50	1.5~10
S	≤0.04	≤0.06	≤0.04	≤0.04	≤0.04	≤0.04	≤0.15
P	≤0.04	≤0.06	≤0.06	≤0.06	≤0.06	≤0.06	≤0.15
Mo	≤0.5	≤0.5	≤0.5	0.10~3.0	0.10~3.0	≤1.0	≤0.10
Cu	0.10~0.60	≤0.25	0.20~0.40	0.10~1.00	0.10~1.00	-	-
Ni	≤0.50	≤0.30	0~0.30	0~0.30	0~0.30	-	3.3~10
Re	≤0.02	≤0.02	≤0.02	-	-	-	-
Equivalent Specifications	DL/T 681-1999 GB/T26651-2011	AS 2074 L2B Mod	DL/T 681-1999	GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401.		GB/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12	GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A
Material Type	Martensite Steel	Martensite or Pearlitic Cr Mo Steel	Martensite Steel	Martensite matrix		Austenitic Mn Steel	-
Hardness	HRc≥48	HB470 & HB 321~370	HRc≥50	HRc≥56		HB≤300	HRc≥56
Impact Value	Ak≥40J	-	Ak≥10J	Ak≥4J		Ak≥80J	-